MM10VC103MCZ2A [KYOCERA AVX]
Medical MLCC;MLCC Medical Applications – MM Series
General Specifications
The AVX MM series is a multi-layer ceramic capacitor designed for use in medical applications other than
implantable/life support. These components have the design & change control expected for medical devices
and also offer enhanced LAT including reliability testing and 100% inspection.
APPLICATIONS
Implantable, Non-Life Supporting Medical Devices
• e.g. implanted temporary cardiac monitor, insulin pumps
External, Life Supporting Medical Devices
• e.g. heart pump external controller
External Devices
• e.g. patient monitoring, diagnostic equipment
HOW TO ORDER
MM02
Z
A
100
J
G
T
3
A
Capacitance
Tolerance
Size
Rated
Dielectric
Code
A = NP0 (C0G)
C = X7R
Capacitance
Code (In pF)
(2 significant
digits + number
of zeros)
for values <10pF:
letter R denotes
decimal point.
Example:
68pF = 680
8.2pF = 8R2
Failure Rate
C = Standard
Range
Termination
Finish
Packaging
Special
Code
2 = 7" Reel
MM02 = 0402 Voltage
MM03 = 0603 Z = 10V
MM05 = 0805 Y = 16V
MM06 = 1206 3 = 25V
MM10 = 1210 5 = 50V
MM08 = 1808 1 = 100V
MM12 = 1812 2 = 200V
MM20 = 2220 V = 250V
7 = 500V
4 = 13" Reel A = Standard
B = ±0.1pF
T =Plated Ni & Sn
(NP0 only)
C = ±0.25pF
D = ±0.5pF
F = ±1% (≥10pF)
G = ±2% (≥10pF)
J = ±5%
K = ±10%
M = ±20%
Contact AVX
for others
Contact AVX
for others
Z =Flexiterm
(X7R only)
COMMERCIAL VS MM SERIES PROCESS COMPARISON
Commercial
MM Series
Standard part numbers; no restriction on
Specific series part number, used to control supply
of product
Administrative
who purchases these parts
Minimum ceramic thickness of 0.020" on all
X7R product
Design
Minimum ceramic thickness of 0.022" (0.56mm)
Side & end margins = 0.004" min
Cover layers = 0.003" min
Dicing
Side & end margins = 0.003" min
Lot Qualification Destructive
Physical Analysis (DPA)
As per EIA RS469
Increased sample plan – stricter criteria
Visual/Cosmetic Quality
Application Robustness
Standard process and inspection
100% inspection
Standard sampling for accelerated wave
solder on X7R dielectrics
Increased sampling for accelerated wave solder on
X7R and NP0 followed by lot by lot reliability testing
AVX will qualify and notify customers before
making any change to the following materials or
processes:
• Dielectric formulation, type, or supplier
• Metal formulation, type, or supplier
• Termination material formulation, type, or supplier
• Manufacturing equipment type
Required to inform customer of changes in:
• form
• fit
Design/Change Control
• function
• Quality testing regime including sample size and
accept/ reject criteria
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
114
040721
MM Series – MLCC for Medical Applications
NP0 (C0G) – Specifications & Test Methods
Parameter/Test
NP0 Specification Limits
Measuring Conditions
Operating Temperature Range
-55ºC to +125ºC
Within specified tolerance
<30 pF: Q≥ 400+20 x Cap Value
≥30 pF: Q≥ 1000
Temperature Cycle Chamber
Capacitance
Freq.: 1.0 MHz ± 10% for cap ≤ 1000 pF
1.0 kHz ± 10% for cap > 1000 pF
Voltage: 1.0Vrms ± .2V
Q
100,000MΩ or 1000MΩ - μF,
Charge device with rated voltage for
Insulation Resistance
whichever is less
60 ± 5 secs @ room temp/humidity
Charge device with 300% of rated voltage for
1-5 seconds, w/charge and discharge current
limited to 50 mA (max)
Dielectric Strength
No breakdown or visual defects
Note: Charge device with 150% of rated voltage
for 500V devices.
Appearance
Capacitance
No defects
Deflection: 2mm
Test Time: 30 seconds
±5% or ±.5 pF, whichever is greater
Variation
Resistance to
Flexure
Q
Meets Initial Values (As Above)
≥ Initial Value x 0.3
Stresses
Insulation
Resistance
≥ 95% of each terminal should be covered
with fresh solder
No defects, <25% leaching of either end terminal
Dip device in eutectic solder at 230 ± 5ºC
for 5.0 ± 0.5 seconds
Solderability
Appearance
Capacitance
≤ ±2.5% or ±.25 pF, whichever is greater
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Variation
Dip device in eutectic solder at 260ºC for 60
seconds. Store at room temperature for 24 ± 2
hours before measuring electrical properties.
Q
Resistance to
Solder Heat
Insulation
Resistance
Dielectric
Meets Initial Values (As Above)
No visual defects
Strength
Appearance
Step 1: -55ºC ± 2º
30 ± 3 minutes
≤ 3 minutes
Capacitance
≤ ±2.5% or ±.25 pF, whichever is greater
Step 2: Room Temp
Variation
Q
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Step 3: +125ºC ± 2º
Step 4: Room Temp
30 ± 3 minutes
≤ 3 minutes
Thermal
Shock
Insulation
Resistance
Dielectric
Repeat for 5 cycles and measure after
24 hours at room temperature
Meets Initial Values (As Above)
No visual defects
Strength
Appearance
Capacitance
≤ ±3.0% or ± .3 pF, whichever is greater
Charge device with twice rated voltage in test
chamber set at 125ºC ± 2ºC
Variation
≥ 30 pF:
≥10 pF, <30 pF:
<10 pF:
Q≥ 350
for 1000 hours (+48, -0).
Q
Q≥ 275 +5C/2
Q≥ 200 +10C
Load Life
Remove from test chamber and stabilize at
room temperature for 24 hours
before measuring.
Insulation
≥ Initial Value x 0.3 (See Above)
Resistance
Dielectric
Strength
Meets Initial Values (As Above)
Appearance
No visual defects
Capacitance
≤ ±5.0% or ± .5 pF, whichever is greater
Variation
Store in a test chamber set at 85ºC ± 2ºC/ 85%
± 5% relative humidity for 1000 hours
(+48, -0) with rated voltage applied.
≥ 30 pF:
≥10 pF, <30 pF:
<10 pF:
Q≥ 350
Q
Q≥ 275 +5C/2
Q≥ 200 +10C
Load
Humidity
Remove from chamber and stabilize at room
temperature for 24 ± 2 hours before measuring.
Insulation
≥ Initial Value x 0.3 (See Above)
Meets Initial Values (As Above)
Resistance
Dielectric
Strength
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
115
113016
MM Series – MLCC for Medical Applications
NP0/C0G Capacitance Range
PREFERRED SIZES ARE SHADED
SIZE
0603
0805
1206
WVDC 16
0R5
1R0
1R2
1R5
1R8
2R2
2R7
3R3
3R9
4R7
5R6
6R8
8R2
100
120
150
180
220
270
330
390
470
560
680
820
101
121
151
181
221
271
331
391
471
561
681
821
102
122
152
25
50
100
16
25
50
100
16
25
50
100
Cap
(pF)
0.5
1.0
1.2
1.5
1.8
2.2
2.7
3.3
3.9
4.7
5.6
6.8
8.2
10
12
15
18
22
27
33
39
47
56
68
82
100
120
150
180
220
270
330
390
470
560
680
820
1000
1200
1500
WVDC
16
25
50
100
16
25
50
100
16
25
50
100
SIZE
0603
0805
1206
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
116
113016
MM Series – MLCC for Medical Applications
X7R Specifications and Test Methods
Parameter/Test
X7R Specification Limits
Measuring Conditions
Operating Temperature Range
-55ºC to +125ºC
Within specified tolerance
Temperature Cycle Chamber
Capacitance
≤ 10% for ≥ 50V DC rating
Freq.: 1.0 kHz ± 10%
≤ 12.5% for 25V DC rating
Voltage: 1.0Vrms ± .2V
Q
≤ 12.5% for 25V and 16V DC rating
≤ 12.5% for ≤ 10V DC rating
100,000MΩ or 1000MΩ - μF,
Charge device with rated voltage for 120 ± 5
secs @ room temp/humidity
Insulation Resistance
whichever is less
Charge device with 300% of rated voltage for
1-5 seconds, w/charge and discharge current
limited to 50 mA (max)
Dielectric Strength
No breakdown or visual defects
Note: Charge device with 150% of rated voltage
for 500V devices.
Appearance
Capacitance
No defects
≤ ±12%
Deflection: 2mm
Test Time: 30 seconds
Variation
Resistance to
Flexure
Dissipation
Meets Initial Values (As Above)
≥ Initial Value x 0.3
Stresses
Factor
Insulation
Resistance
≥ 95% of each terminal should be covered
with fresh solder
No defects, <25% leaching of either end terminal
Dip device in eutectic solder at 230 ± 5ºC
for 5.0 ± 0.5 seconds
Solderability
Appearance
Capacitance
≤ ±7.5%
Variation
Dissipation
Factor
Dip device in eutectic solder at 260ºC for 60
seconds. Store at room temperature for 24 ± 2
hours before measuring electrical properties.
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Resistance to
Solder Heat
Insulation
Resistance
Dielectric
Meets Initial Values (As Above)
No visual defects
≤ ±7.5%
Strength
Appearance
Step 1: -55ºC ± 2º
30 ± 3 minutes
≤ 3 minutes
Capacitance
Step 2: Room Temp
Variation
Dissipation
Factor
Meets Initial Values (As Above)
Meets Initial Values (As Above)
Step 3: +125ºC ± 2º
Step 4: Room Temp
30 ± 3 minutes
≤ 3 minutes
Thermal
Shock
Insulation
Resistance
Dielectric
Repeat for 5 cycles and measure after
24 ± 2 hours at room temperature
Meets Initial Values (As Above)
No visual defects
Strength
Appearance
Capacitance
Charge device with 1.5 rated voltage (≤ 10V) in
test chamber set at 125ºC ± 2ºC
for 1000 hours (+48, -0)
≤ ±12.5%
Variation
Dissipation
Factor
≤ Initial Value x 2.0 (See Above)
≥ Initial Value x 0.3 (See Above)
Load Life
Remove from test chamber and stabilize at
room temperature for 24 ± 2 hours before
measuring.
Insulation
Resistance
Dielectric
Meets Initial Values (As Above)
No visual defects
Strength
Appearance
Capacitance
≤ ±12.5%
Store in a test chamber set at 85ºC ± 2ºC/ 85%
± 5% relative humidity for 1000 hours
(+48, -0) with rated voltage applied.
Variation
Dissipation
Factor
≤ Initial Value x 2.0 (See Above)
≥ Initial Value x 0.3 (See Above)
Load
Humidity
Insulation
Remove from chamber and stabilize at room
temperature and humidity for
Resistance
24 ± 2 hours before measuring.
Dielectric
Strength
Meets Initial Values (As Above)
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
117
113016
MM Series – MLCC for Medical Applications
X7R Capacitance Range
PREFERRED SIZES ARE SHADED
SIZE
0402
0603
0805
1206
1210
1808
1812
2220
WVDC 16 25 50 10 16 25 50 100 200 10 16 25 50 100 200 250 10 16 25 50 100 200 250 500 10 16 25 50 100 200 250 500 50 100 200 50 100 200 250 25 50 100
Cap
(pF)
220
270
330
390
470
560
680
820
1000
1200
1500
1800
2200
2700
3300
3900
4700
5600
6800
8200
221
271
331
391
471
561
681
821
102
122
152
182
222
272
332
392
472
562
682
822
103
123
153
183
223
273
333
393
473
563
683
823
104
124
154
224
334
474
564
684
824
105
125
155
cap 0.010
uF 0.012
0.015
0.018
0.022
0.027
0.033
0.039
0.047
0.056
0.068
0.082
0.10
0.12
0.15
0.22
0.33
0.47
0.56
0.68
0.82
1.0
1.2
1.5
WVDC
16 25 50 10 16 25 50 100 200 10 16 25 50 100 200 250 10 16 25 50 100 200 250 500 10 16 25 50 100 200 250 500 50 100 200 50 100 200 250 25 50 100
SIZE
0402
0603
0805
1206
1210
1808
1812
2220
The Important Information/Disclaimer is incorporated in the catalog where these specifications came from or
available online at www.avx.com/disclaimer/ by reference and should be reviewed in full before placing any order.
118
110116
相关型号:
©2020 ICPDF网 联系我们和版权申明